Stanford Materials Corporation (SMC) offers high-quality Magnesium – Scandium (Mg-Sc) Master Alloy with different ratios at competitive prices. Magnesium Scandium Master Alloy is made from melted Magnesium and Scandium Metal. The common alloy is MgSc2, MgSc5, MgSc10, MgSc20 and MgSc30.
Magnesium Scandium Master Alloy is made from melted Magnesium and Scandium Metal. The common alloy is MgSc2, MgSc5, MgSc10, MgSc20 and MgSc30.Stanford Advanced Materials provides high purity Magnesium – Scandium (Mg-Sc) Master Alloy at a competitive price.
|
Item |
Purity（%） |
Content of Gd |
|
MA-21-1 |
99.9 |
2 ~ 10 ％ |
|
MA-21-2 |
99.99 |
2 ~ 10 ％ |
|
MA-21-C |
99.9 or 99.99 |
Customized |
Main technical indexes & parameters of high strength and high-temperature resistant rare-earth modified Mg alloy
|
Tensile Strength Rm |
Yield Strength Rp0.2 |
Elongation A5 |
Vickers Hardness |
|
280 - 290 Mpa |
140 - 295 Mpa |
6 – 10% |
67 - 63 |
Rare earth (RE) elements have also been successfully alloyed with Mg. The addition of rare-earth (RE) elements can refine grains and weaken anisotropy to improve the ductility of the Mg alloys. In addition, RE elements give rise to a dispersion of thermally stable precipitates with a high melting point (above 620 °C), an improvement over precipitates of the Mg-Zn system which melt at approximately 340°C and thus have poor thermal stability and exhibit a tendency for hot tearing.